Characterization of Radiation Damage in Carbon Nanotube Field-Effect Transistors

Authors

• Sarah Ashley Francis, Air Force Institute of Technology
• Cory D. Cress, U.S. Naval Research Laboratory
• John W.. McClory, Air Force Institute of Technology
• Elizabeth A. Moore, KBRwyle, Dayton
• James C. Petrosky, Air Force Institute of Technology

Document Type

Article

Publication Date

12-3-2013

Abstract

Carbon nanotube field-effect transistors with Al₂O₃ gate dielectrics have been characterized before and after 1 MeV electron irradiation. Pre-irradiation interface trap densities determined by charge pumping measurements were on the order of 10¹¹ cm^-2eV^-1 . Following irradiation to fluences of 10¹⁶ e/cm2 and 10¹⁷ e/cm², the measured interface trap densities decreased significantly for all devices. This result is largely attributed to the removal of molecular adsorbates that act as trap sites on the nanotubes (de-doping) while the devices are irradiated under vacuum. Negative shifts in the transistor I-V curves with irradiation indicate radiation-induced hole trapping in the gate dielectric, with some recovery after room temperature annealing. No significant changes were observed in the Raman spectra following irradiation, indicating the intrinsic structure of the carbon nanotubes remained unchanged. These results suggest that the radiation response of these devices is dominated by charge trapping in the oxide layers and at the carbon nanotube surfaces. Furthermore, the charge pumping technique can be used as a tool for probing surface adsorbates in carbon nanotube devices, and elucidating their role in the device radiation response.

Comments

The full article is available from IEEE via subscription or purchase, using the DOI link below.

DOI

10.1109/TNS.2013.2284542

Source Publication

IEEE Transactions on Nuclear Science (ISSN 0018-9499)

Recommended Citation

S. A. Francis, C. D. Cress, J. W. McClory, E. A. Moore and J. C. Petrosky, "Characterization of Radiation Damage in Carbon Nanotube Field-Effect Transistors," in IEEE Transactions on Nuclear Science, vol. 60, no. 6, pp. 4087-4093, Dec. 2013, doi: 10.1109/TNS.2013.2284542.